A new approach to prepare highly dispersed calcium aluminate at temperatures from 900°C with desired properties (bulk density starting from 0.015 g/cm3, particle size falling in the range of 7–42 described, which consists of step-by-step heat treatment of a concentrated aqueous solution of Al(NO3)3, Ca(NO3)2, and C6H8O7 in the molar ratio CaO : Al2O3 = 1 : 2. The main stages of the synthesis X-ray powder diffraction, IR spectroscopy, as well as scanning and transmission electron microscopies. dispersed calcium aluminate obtained using the developed approach has pronounced luminescent features.

全文:

受限制的访问

作者简介

L. Kozlova

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

编辑信件的主要联系方式.
Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

I. Voroshilov

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

Yu. Ioni

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

A. Son

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

A. Popova

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

I. Kozerozhets

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: kozzllova167@gmail.com
俄罗斯联邦, Moscow

参考

  1. Zawrah M., Khalil N. // Ceram. Int. 2007. V. 33. P. 1419. https://doi.org/10.1016/j.ceramint.2006.04.022
  2. Kozerozhets I.V., Avdeeva V.V., Buzanov G.A. et al. // Inorganics. 2022. V. 10. № 212. P. 212. https://doi.org/10.3390/inorganics10110212
  3. Bai J., Liu J., Li C. et al. // Adv. Powder. Technol. 2011. V. 22. P. 72. https://doi.org/10.1016/j.apt.2010.03.013
  4. Ying S., Guan Z., Ofoegbu P.C. et al. // Environ. Technol. InnoV. 2022. V. 26. P. 102336. https://doi.org/10.1016/j.eti.2022.102336
  5. Pourgolmohammad B., Masoudpanah S.M., Aboutalebi M.R. // Ceram. Int. 2017. V. 43. P. 3797. https://doi.org/10.1016/j.ceramint.2016.12.027
  6. Fang L. // Int. J. Electrochem. Sci. 2017. V. 12. P. 218. https://doi.org/10.20964/2017.01.07
  7. Mu X., Chen Y., Edward Lester E. et al. // Microporous Mesoporous Mater. 2018. V. 270. P. 249. https://doi.org/10.1016/j.micromeso.2018.05.027
  8. Hussain S.K., Yu J.S. // J. Lumin. 2017. V. 183. P. 39. https://doi.org/10.1016/j.jlumin.2016.11.003
  9. Singh D., Sheoran S., Tanwar V. // Adv. Mater. Lett. 2017. V. 8. P. 656. https://doi.org/10.5185/amlett.2017.7011
  10. Pollmann H. // Rev. Mineral. Geochem. 2012. V. 74. P. 1. https://doi.org/10.2138/rmg.2012.74.1
  11. Kozlova L.O., Ioni Yu.V., Son A.G. et al. // Russ. J. Inorg. Chem. 2023. V. 68. P. 1744. https://doi.org/10.1134/S0036023623602374
  12. Tian Y., Pan X., Yu H. et al. // J. Alloys Compd. 2016. V. 670. P. 96. https://doi.org/10.1016/j.jallcom.2016.02.059
  13. Emmett M. // Dial. Transplant. 2006. V. 35. P. 284. https://doi.org/10.1002/dat.20018
  14. Aitasalo T., Durygin A., Hölsä J. et al. // J. Alloys Compd. 2004. V. 380. P. 4. https://doi.org/10.1016/j.jallcom.2004.03.007
  15. Gülgün M., Popoola O., Waltraud M. et al. // J. Am. Ceram. Soc. 1997. V. 77. P. 531. https://doi.org/10.1111/j.1151-2916.1994.tb07026.x
  16. Yu H., Pan X., Wang B. et al. // Trans. Nonferrous Met. Soc. China. 2012. V. 22. P. 3108. https://doi.org/10.1016/S1003-6326(11)61578-1
  17. Zhang D., Pan X., Yu H. et al. // J. Mater. Sci. Technol. 2015. V. 31. P. 1244. https://doi.org/10.1016/j.jmst.2015.10.012
  18. Fujii K., Kondo W., Ueno H. et al. // J. Am. Ceram. Soc. 1986. V. 69. P. 361. https://doi.org/10.1111/j.1151-2916.1986.tb04748.x
  19. Edmonds R., Majumdar A. // Cem. Concr. Res. 1988. V. 18. P. 311. https://doi.org/10.1016/0008-8846(88)90015-4
  20. Chen G. // J. Alloys Compd. 2006. V. 416. P. 279. https://doi.org/10.1016/j.jallcom.2005.08.059
  21. Iftekhar S., Grins J., Svensson G. et al. // J. Eur. Ceram. Soc. 2008. V. 28. P. 747. https://doi.org/10.1016/j.jeurceramsoc.2007.08.012
  22. Ridwan I., Asmi D. // AIP Conf. Proc. 2008. V. 989. P. 180. https://doi.org/10.1063/1.2906060
  23. Mohamed B., Sharp J. // Thermochim. Acta. 2002. V. 388. P. 105. https://doi.org/10.1016/S0040-6031(02)00035-7
  24. Jerebtsov D., Mikhailov G. // Ceram. Int. 2001. V. 27. P. 25. https://doi.org/10.1016/S0272-8842(00)00037-7
  25. Kozerozhets I.V., Panasyuk G.P., Semenov E.A. et al. // Powder Technol. 2023. V. 413. P. 118030. https://doi.org/10.1016/j.powtec.2022.118030
  26. Escribano P., Marchal M., Sanjuán L. et al. // J. Solid State Chem. 2005. V. 178. P. 1978. https://doi.org/10.1016/j.jssc.2005.04.001
  27. Stephan D., Wilhelm P. // Z. Anorg. Allg. Chem. 2004. V. 630. P. 1477. https://doi.org/10.1002/zaac.200400090
  28. Kozerozhets I.V., Panasyuk G.P., Semenov E.A. et al. // Ceram. Int. 2022. V. 48. P. 7522. https://doi.org/10.1016/j.ceramint.2021.11.296
  29. Ranjbar A., Rezaei M. // Adv. Powder. Technol. 2014. V. 25. P. 467. https://doi.org/10.1016/j.apt.2013.07.011
  30. Kingsley J.J., Patil K.C. // Mater. Lett. 1988. V. 6. P. 427. https://doi.org/10.1016/0167-577x(88)90045-6
  31. Goswami B., Ranil N., Ahlawat R. // J. Mountain Res. 2021. V. 16. P. 53. https://doi.org/10.51220/jmr.v16i2.8
  32. Goswami B., Rani N., Jangra N. et al. // J. Nanopart. Res. 2023. V. 25. P. 72. https://doi.org/10.1007/s11051-023-05718-1
  33. Kozerozhets I.V., Semenov E.A., Kozlova L.O. et al. // Mater. Chem. Phys. 2023. V. 309. P. 128387. https://doi.org/10.1016/j.matchemphys.2023.128387
  34. Norton A.M., Nguyen H., Xiao N.L. et al. // RSC Adv. 2018. V. 8. P. 17101. https://doi.org/10.1039/c8ra03088j

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Scheme of synthesis of nanoscale CaAl2O4 powder

下载 (104KB)
索引源数据
3. Fig. 2. IR absorption spectra of samples obtained at different stages of heat treatment of carbon-containing xerogel based on Ca2+ and Al3+ nitrates at temperatures 130 (1), 300 (2), 400 (3), 500 (4), 900 (5), 1000 (6) and 1100°С (7)

下载 (206KB)
索引源数据
4. Fig. 3. Diffractograms of samples obtained after heat treatment of carbon-containing xerogel based on Ca2+ and Al3+ nitrates at temperatures 500 (1), 900 (2), 1000 (3), 1100 (4) and 1250°C (5)

下载 (250KB)
索引源数据
5. Fig. 4. SEM images of a sample obtained after heat treatment of carbon-containing gel Ca2+ and Al3+ at temperatures of 300 (a) and 500°C (b)

下载 (228KB)
索引源数据
6. Fig. 5. TEM (a) and SEM images (b) of a sample obtained after heat treatment of carbonaceous xerogel Ca2+ and Al3+ at a temperature of 900°C

下载 (282KB)
索引源数据
7. Fig. 6. TEM (a) and SEM images (b) of a sample obtained after heat treatment of carbonaceous xerogel Ca2+ and Al3+ at a temperature of 1000°C

下载 (322KB)
索引源数据
8. Fig. 7. Luminescence spectra of calcium aluminate samples at λexc = 238 (a) and 390 nm (b)

下载 (186KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024