Synthesis and study of dense materials in the Zr–Al–C system

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Рұқсат ақылы немесе тек жазылушылар үшін

Аннотация

The initial powders Zr, Al, C and Zr, Al, Sc were used for the synthesis of MAX phases of the composition Zr2AlC and Zr3AlC2. The highest content (50.4 vol%) of the MAX phase Zr3AlC2 was obtained using the initial powders Zr/Al/Zr in the ratio of components 1:1.5:2 with the addition of 5 vol% Al. The optimal temperature for the synthesis of a material based on the MAX phase Zr2AlC is 1525° C, a material based on Zr3AlC2 is 1575°C. The structure of the synthesized MAX materials obtained includes elongated grains of the composition Zr2AlC and Zr3AlC2, which determines their high strength. Zirconium carbide, as an intermediate phase, is always present in the final products. Due to the large evaporation of aluminum, the ZrO2 phase is also present in the synthesis products. Excess aluminum contributes to the greatest formation of Zr2AlC and Zr3AlC2 phases during synthesis.

Авторлар туралы

I. Arlashkin

St. Petersburg State Institute of Technology (Technical University);I.V. Grebenshchikov Institute of Silicate Chemistry of the Russian Academy of Sciences

Email: iarlashkin@mail.ru

S. Perevislov

I.V. Grebenshchikov Institute of Silicate Chemistry of the Russian Academy of Sciences

V. Stolyarova

I.V. Grebenshchikov Institute of Silicate Chemistry of the Russian Academy of Sciences;St. Petersburg State University

Әдебиет тізімі

  1. Медведева Н.И., Еняшин А.Н., Ивановский А.Л. // ЖCХ. 2011. Т. 52. № 4. С. 806
  2. Medvedeva N.I., Enyashin A.N., Ivanovskii A.L. // J. Struct. Chem. 2011. Vol. 52. P. 785. doi: 10.1134/S0022476611040226
  3. Barsoum M.W. // Progress Solid State Chem. 2000. Vol. 28. N 1-4. P. 201. doi: 10.1016/S0079-6786(00)00006-6
  4. Istomin P.V., Nadutkin A.V., Ryabkov Y.I., Goldin B.A. // Inorg. Mater. 2006. Vol. 42. N 3. P. 250. doi: 10.1134/S0020168506030071
  5. Zhang Z.F., Sun Z.M., Hashimoto H. // Mater. Lett. 2003. Vol. 57. N 7. P. 1295. doi: 10.1016/S0167-577X(02)00974-6
  6. El-Raghy T., Barsoum M.W. // J. Am. Ceram. Soc. 1999. Vol. 82. N 10. P. 2849. doi: 10.1111/j.1151-2916.1999.tb02166.x
  7. Gao N.F., Miyamoto Y., Zhang D. // J. Mater. Sci. 1999. Vol. 34. N 18. P. 4385. doi: 10.1023/A:1004664500254
  8. Jeitschko W., Nowotny H., Benesovsky F. // Monatsh. Chem. 1964. Vol. 95. N 1. P. 178. doi: 10.1007/BF00913068
  9. Perevislov S.N., Sokolova T.V., Stolyarova V.L. // Mater. Chem. Phys. 2021. Vol. 267. P. 124625. doi: 10.1016/j.matchemphys.2021.124625
  10. Bykova A.D., Semenova V.V., Perevislov S.N., Markov M.A. // Refract. Ind. Ceram. 2021. Р. 89. doi: 10.1007/s11148-021-00564-x
  11. Перевислов С.Н., Семенова В.В., Лысенков А.С. // ЖНХ. 2021. Т. 66. № 8. С. 987
  12. Perevislov S.N., Semenova V.V., Lysenkov A.S. // Russ. J. Inorg. Chem. 2021. Vol. 66. N 8. Р. 1100. doi: 10.1134/S0036023621080210
  13. Perevislov S.N., Arlashkin I.E., Lysenkov A.S. // Refract. Ind. Ceram. 2022. P. 215. doi: 10.1007/s11148-022-00709-6
  14. Lapauw T., Lambrinou K., Cabioc'h T., Halim J., Lu J., Pesach A., Rivinf O., Ozeri O., Caspi E.N., Hultman L., Eklund P., Rosén J., Barsoum M.W., Vleugels J. // J. Eur. Ceram. Soc. 2016. Vol. 36. N 8. P. 1847. doi: 10.1016/j.jeurceramsoc.2016.02.044
  15. Lapauw T., Halim J., Lu J., Cabioc'h T., Hultman L., Barsoum M.W., Lambrinou K., Vleugels J. // J. Eur. Ceram. Soc. 2016. Vol. 36. N 3. P. 943. doi: 10.1016/j.jeurceramsoc.2015.10.011
  16. Okamoto H. // J. Phase Equilib. Diff. 2002. Vol. 23. N 5. P. 455. doi: 10.1361/105497102770331497
  17. Wang T., Jin Z., Zhao J.C. // J. Phase Equilib. 2001. Vol. 22. N 5. P. 544. doi: 10.1007/s11669-001-0072-4

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу

© Russian Academy of Sciences, 2023