Influence of copper powder structure on the catalytic properties of cerium oxide

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

The influence of the structure of copper powder particles on the catalytic activity of the CeO2/Cu catalyst was studied using the methods of X-Ray diffraction, electron microscopy, electron diffraction, energy dispersive X-Ray analysis, as well as programmed temperature reduction of CO (CO-TPR). Nanocomposites were obtained by mechanochemical synthesis using copper particles differing in size and morphology: micron-sized dendrites and nanoparticles. It was shown that the activity of the catalyst obtained from nanosized copper is two times higher, which is due to the presence of CuxO clusters located on the atomic steps of cerium oxide nanocrystals. This arrangement of clusters apparently ensures that the activating centers are not blocked. Thus, the surface structure of cerium oxide particles formed when using nanosized copper powder is a key factor responsible for the catalytic activity.

全文:

受限制的访问

作者简介

O. Zhigalina

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

编辑信件的主要联系方式.
Email: zhigal@crys.ras.ru
俄罗斯联邦, Moscow

O. Morozova

N.N. Semenov Federal Research Center for Chemical Physics RAS

Email: zhigal@crys.ras.ru
俄罗斯联邦, 4, Kosygin st., 119991 Moscow

D. Khmelenin

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: zhigal@crys.ras.ru
俄罗斯联邦, Moscow

E. Cherkovskiy

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: zhigal@crys.ras.ru
俄罗斯联邦, Moscow

A. Firsova

N.N. Semenov Federal Research Center for Chemical Physics RAS

Email: zhigal@crys.ras.ru
俄罗斯联邦, 4, Kosygin st., 119991 Moscow

V. Basu

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: zhigal@crys.ras.ru
俄罗斯联邦, Moscow

G. Vorobieva

N.N. Semenov Federal Research Center for Chemical Physics RAS

Email: zhigal@crys.ras.ru
俄罗斯联邦, 4, Kosygin st., 119991 Moscow

参考

  1. Soria J., Conesa J.C., Martinez-Arias A., Coronado J.M. // Solid State Ionics. 1993. V. 65. P. 755. https://doi.org/10.1016/0167-2738(93)90191-5
  2. James T.E., Hemmingson S.L., Ito T., Campbell C.T. // J. Phys. Chem. 2015. V. 119. P. 17209. https://doi.org/10.1021/acs.jpcc.5b04621
  3. Lu J., Wang J., Zou Q. et al. // ACS Catal. 2019. V. 9. № 3. P. 2177. https://doi.org/10.1021/acscatal.8b04035
  4. Konsolakis M., Lykaki M. // Catalysts. 2021. V. 11. № 4. P. 452. https://doi.org/10.3390/catal11040452
  5. Varvoutis G., Lykaki M., Marnellos G.E., Konsolakis M. // Catalysts. 2023. V. 13. P. 275. https://doi.org/10.3390/catal13020275
  6. Фирсова А.А., Морозова О.С., Леонов А.В. и др. // Кинетика и катализ. 2014. Т. 55. № 6. С. 783. https://doi.org/10.7868/S0453881114060069
  7. Borchers Ch., Martin M.L., Vorobjeva G.A. et al. // J. Nanopart. Res. 2016. V. 18. P. 344. https://doi.org/10.1007/s11051-016-3640-6
  8. Морозова О.С., Фирсова А.А., Тюленин Ю.П. и др. // Кинетика и катализ. 2020. Т. 61. № 5. P. 741. https://doi.org/10.31857/S0453881120050081
  9. Zhigach A.N., Kuskov M.L., Leipunskii I.O. et al. // Bulletin of the Russian Academy of Sciences: Energetic. 2012. V. 3. P. 80.
  10. Shelekhov E.V., Sviridova T.A. // Met. Sci. Heat Treat. 2000. V. 42. P. 309. https://doi.org/10.1007/BF02471306
  11. Konsolakis M. // Appl. Catal. B: Enviromental. 2016. V. 198. P. 49. https://doi.org/10.1016/j.apcatb.2016.05.037
  12. Van Deelen T.W., Mejía C.H., De Jong K.P. // Nature Catal. 2019. V. 2. P. 955. https://doi.org/10.1038/s41929-019-0364-x
  13. Cipriano L.A., Di Liberto G., Pacchioni G. // ACS Catal. 2022. V. 12. № 19. P. 11682. https://doi.org/10.1021/acscatal.2c03020
  14. Gao Y., Zhang L., Van Hoof A.J.F., Hensen E.J.M. // Appl. Catal. A. General. 2020. V. 602. P. 117712. https://doi.org/10.1016/j.apcata.2020.117712
  15. Cruz A.R.M., Assaf E.M., Gomes J.M., Assaf J.M. // Catal. Today. 2021. V. 381. № 1. P. 42. https://doi.org/10.1016/j.cattod.2020.09.007
  16. Borchers Ch., Martin M.L., Vorobjeva G.A. et al. // AIP Adv. 2019. V. 9. P. 065115. https://doi.org/10.1063/1.5109067
  17. Paier J., Penschke C., Sauer J. // Chem. Rev. 2013. V. 113. P. 3949. https://doi.org/10.1021/cr3004949
  18. Chen A., Yu X., Zhou Y. et al. // Nature Catalysis. 2019. V. 2. P. 334. https://doi.org/10.1038/s41929-019-0226-6
  19. Puigdollers A.R., Schlexer P., Tosoni S., Pacchioni G. //ACS Catal. 2017. V. 7. P. 6493. https://doi.org/10.1021/acscatal.7b01913
  20. Kappis K., Papavasiliou J. // ChemCatChem. 2019. V. 11. № 19. P. 4765. https://doi.org/10.1002/cctc.201901108
  21. Martínez-Munuera J.C., Javier G.M., Yeste M.P. et al. // Appl. Surf. Sci. 2022. V. 575. P. 151717. https://doi.org/10.1016/j.apsusc.2021.151717

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Structure of the initial CeO2 powder: bright-field TEM image of a single-crystal particle (a), TP TEM image of a polycrystalline particle (b), energy-dispersive spectrum (c).

下载 (215KB)
索引源数据
3. Fig. 2. SEM images of the initial powders: CeO2 (a), dendritic copper Cu(M) obtained by the electrochemical method (b), copper Cu(N) obtained by the levitation-jet method (c).

下载 (177KB)
索引源数据
4. Fig. 3. Microstructure of Cu(N) powder particles: particle chains (a), HRTEM image of the core and shell of an individual particle (b), STEM image and distribution maps of copper and oxygen for individual particles (c–d), energy-dispersive spectrum (e).

下载 (357KB)
索引源数据
5. Fig. 4. Temperature dependence of CO conversion: Cu(M)–CeO2 (1), Cu(N)–CeO2 (2).

下载 (74KB)
索引源数据
6. Fig. 5. Structure of CeO2 powder particles after grinding in a ball mill: TP image of general appearance (a), HRTEM image of individual particles (arrows indicate monatomic steps) (b), microelectron diffraction pattern (c).

下载 (243KB)
索引源数据
7. Fig. 6. Structure of the Cu(N)–CeO2 composite after electron beam irradiation for 10 min: HRTEM image (a), EDS mapping (red – copper, green – cerium) (b).

下载 (261KB)
索引源数据
8. Fig. 7. Structure of the Cu(M)–CeO2 composite under electron beam irradiation for 10 min: HRTEM image (a), EDS mapping (red – copper, green – cerium) (b).

下载 (282KB)
索引源数据
9. Fig. 8. CO-TPR curves for Cu(N)–CeO2 catalysts: 1 – dependence of the mass spectrometer signal intensity (m/e = 44, CO2) on temperature (the MS signal intensity was normalized to the sample mass), 2 – change in sample mass depending on temperature.

下载 (120KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024